Festigkeitswerte verschiedener Aluminiumgusslegierungen
| Werkstoff | Werkstoffeigenschaften | |||||
| Kurzzeichen | Nummer | Block-Nr. | RP0,2 | Rm | A5 | HB 5/250 |
| G-AlSi8Cu3 | 3.2163 | 226 A | 100 – 150 (100) |
160 – 200 (140) |
1 – 3 (0,5) |
65 – 90 (60) |
| G-AlSi12 | 32.581 | 230 A | 70 – 100 (70) |
150 – 200 (140) |
5 – 10 (3) |
45 – 60 (45) |
| G-AlSi5Mg | 32.341 | 235 | 100 – 130 (90) |
140 – 180 (130) |
1 – 3 (0,5) |
55 – 70 (55) |
| G-AlSi10Mg | 3.2381.01 | 239 | 80 – 110 (70) |
160 – 210 (150) |
2 – 6 (2) |
50 – 60 (50) |
| G-AlSi10Mg wa | 3.2381.61 | 239 wa | 180 – 260 (170) |
220 – 320 (200) |
1 – 4 (1) |
80 – 110 (75) |
| G-AlZn10Si8Mg | 230/41oCu | 170 – 200 | 180 – 220 | 1 – 2 | 100 – 110 | |
| G-AlZn10Si8Mg H | 34.311 | Unifont 90 | 200 – 230 (170) |
220 – 250 (180) |
1 – 2 (1) |
90 – 100 (90) |
| G-AlCu4Ti wa | 31.841 | Alufont 52 | 300 – 420 (280) |
400 – 475 (350) |
3 – 4 (2) |
125 – 145 (120) |
| G-AlSi7Mg ta T64 | 32.371 | Antic.-70 | 120 – 170 (120) |
200 – 270 (200) |
4 – 10 (4) |
60 – 80 (55) |
| G-AlSi7Mg wa T6 | 32.371 | Antic.-70 | 200 – 220 (200) |
240 – 320 (240) |
3 – 6 (2,5) |
80 – 110 (80) |
| G-AlMg3Si | 3.3241.01 | 243 | 80 – 100 (70) |
140 – 190 (130) |
3 – 8 (3) |
50 – 60 (45) |
| G-AlMg3Si wa | 3.3241.61 | 243 wa | 120 – 160 (120) |
140 – 190 (130) |
2 – 8 (2) |
65 – 90 (60) |
wa bzw. ta => die Festigkeitswerte werden erst nach einer Wärmebehandlung erzielt
( ) = Mindestwerte im Gußstück mit Wanddicken bis zu 20 mm